[ TPS® PA聚醯胺 尼龍系列 ]
典型工業塑料
尼龍（聚醯胺）具有優良的機械性質、耐摩擦磨損性、耐化學藥品性（有機溶劑）、耐油性、氣體阻隔性。它是一種由於其化學結構而具有高熔點和高吸水性的樹脂。尼龍吸水後，其柔韌性和抗衝擊性會提高。尼龍66比尼龍6具有更低的吸水性和更高的剛性。
▌PA6尼龍物性表比較
| 特性Properties |
測試方法 Test Method |
單位 Unit |
Nylon6 NC |
Nylon6 G30 |
Nylon6 CF |
| 物理性質 Physical Properties | |||||
| 比重 Specific Gravity (23°C) |
ASTM D-792 |
--- | 1.14 | 1.36 | 1.22 |
| 吸水率 Water absorption (23°C， 24 Hrs) |
ASTM D-570 |
% | 1.8 | 1.1 | 1.8 |
| 線膨脹係數 Linear expansion coefficient |
JIS K7197 |
×10 -5 /℃ |
8.0 | 2.0~3.0 | 3.0 |
| 熱傳導 Thermal conduction | E 1530 | W/mK | -- | 0.38 | -- |
| 可燃性 Flammability (UL) | D570 | --- |
HB |
HB |
HB |
| 機械性質 Mechanical Properties | |||||
| 抗拉強度 Tensile strength |
ASTM D-638 |
MPa | 75 | 185 | 180 |
| 拉伸彈性 Tensile elasticity |
ASTM D-638 |
% | 200< | 5.0 | 5.0 |
| 彎曲彈性率 Flexural Modulus |
ASTM D-790 |
GPa | 2.50 | 8.80 | 11.50 |
| 彎曲強度 Flexural Strength |
ASTM D-790 |
MPa | 100 | 260 | 270 |
| 蒲松氏比 Poisson's ratio | -- | --- | 0.38 | 0.35 | -- |
| 抗壓強度 Compressive strength |
ASTM D-695 |
MPa | - | -- | -- |
| 缺口衝擊強度 Izod Notched Impact Strength |
ASTM D-256 |
J/M | 70.0 | 125.0 | -- |
| 洛氏硬度 Rockwell hardness |
ASTM D-785 |
--- | R112 | R120 | -- |
| 熱性質 Thermal Properties | |||||
| 載重撓曲溫度 Deflection temperature under load (1.82 MPa) |
ASTM D-648 |
℃ | 65 | 215 | 200 |
| 連續使用溫度 Continuous use temperature | -- | ℃ | 70 | 100 | -- |
| 玻璃化轉變溫度 Glass transition temperature | -- | ℃ | -- | -- | -- |
| 熔點 Melting point | -- | ℃ | 225 | 225 | 225 |
| 電氣性能 Flammability | |||||
| 介電強度 Dielectric strength (3mm) |
ASTM D-149 |
MV/m | 20.0 | 20.0 | -- |
| 表面電阻 Surface resistance |
ASTM D-257 |
Ω | -- | -- | 10¹ |
| 體積電阻 Volume resistance |
ASTM D-257 |
Ω・cm | 10¹²~10¹³ | 10¹³ | 10⁰~10¹ |
| 介電常數 Permittivity 106Hz |
ASTM D-150 |
--- | 3.4 | 4.0 | -- |
| 介電正切 Dielectric tangent 106Hz |
ASTM D-150 |
--- | 0.03 | 0.03 | -- |
▌PA66尼龍物性表比較
| 特性 Properties |
測試方法 Test Method |
單位 Unit |
Nylon66 NC |
Nylon66 G30 |
| 物理性質 Physical Properties | ||||
| 比重 Specific Gravity (23°C) |
ASTM D-792 |
--- | 1.14 | 1.37 |
| 吸水率 Water absorption (23°C， 24 Hrs) |
ASTM D-570 |
% | 1.2 | 0.6 |
| 線膨脹係數 Linear expansion coefficient |
JIS K7197 |
×10 -5 /℃ |
8.1 | 2.0~3.0 |
| 熱傳導 Thermal conduction | E 1530 | W/mK | 0.25 | 0.40 |
| 可燃性 Flammability (UL) | D570 | --- |
H |
HB |
| 機械性質 Mechanical Properties | ||||
| 抗拉強度 Tensile strength |
ASTM D-638 |
MPa | 86 | 190 |
| 拉伸彈性 Tensile elasticity |
ASTM D-638 |
% | 90.0 | 4.5 |
| 彎曲彈性率 Flexural Modulus |
ASTM D-790 |
GPa | 2.83 | 9.00 |
| 彎曲強度 Flexural Strength |
ASTM D-790 |
MPa | 118 | 275 |
| 蒲松氏比 Poisson's ratio | -- | --- | -- | -- |
| 抗壓強度 Compressive strength |
ASTM D-695 |
MPa | -- | -- |
| 缺口衝擊強度 Izod Notched Impact Strength |
ASTM D-256 |
J/M | 64.0 | 110.0 |
| 洛氏硬度 Rockwell hardness |
ASTM D-785 |
--- | R117 | R121 |
| 熱性質 Thermal Properties | ||||
| 載重撓曲溫度 Deflection temperature under load (1.82 MPa) |
ASTM D-648 |
℃ | 90 | 255 |
| 連續使用溫度 Continuous use temperature | -- | ℃ | -- | 110 |
| 玻璃化轉變溫度 Glass transition temperature | -- | ℃ | 78 | -- |
| 熔點 Melting point | -- | ℃ | 225 | 265 |
| 電氣性能 Flammability | ||||
| 介電強度 Dielectric strength (3mm) |
ASTM D-149 |
MV/m | -- | 20.0 |
| 表面電阻 Surface resistance |
ASTM D-257 |
Ω | -- | -- |
| 體積電阻 Volume resistance |
ASTM D-257 |
Ω・cm | 10¹⁴ | 10¹³ |
| 介電常數 Permittivity 106Hz |
ASTM D-150 |
--- | 3.6 | 3.9 |
| 介電正切 Dielectric tangent 106Hz |
ASTM D-150 |
--- | 0.03 | 0.02 |